Product

Standard

Weld Metal Analysis

Applications

Mechanical Properties

AWS: E Ni Cu B

DIN 8573: E Ni Cu G 2

Current: = (+) / ~

–

A successful electrode for “cold” welding grey, malleable and cast iron. Special thin coating for minimum heat insures fully machinable deposit, completely free from porosity.

T: 240 – 290 N/mm²————–

H: 190 HB

AWS: E 7013 G

ISO 3580: E Mo R
DIN 8575: E Mo R 22

Rutile-basic coated electrode for high tensile and high temperature steel. The weld deposit is tough and non-ageing.

Suitable for materials:
St45,8, St50, St55,4, 17Mn4, 19Mn5, 15Mo3, HIII, HIV, WStE 36

T: 520 – 620 N/mm²

Y: 440 – 490 N/mm²
E(1=5d): 22 – 28 %

I: 63 – 80 Joule

AWS: E 7018 A 1

DIN 8575: E Mo B 20+

–

Lime-basic coated electrode for high tensile and high temperature steel. The weld deposit is tough and non-ageing.

AWS: E 8013 G
ISO 3580: E 1 Cr Mo R
DIN 8575:E Cr Mo 1 R 22

BS: 2493 Type B

Current: = (+) / ~

C: 0,07 %
Si: 0,35 %
Mn: 0,65 %

Cr: 1 %

Mo: 0,5 %

Rutile basic coated electrode for high quality weld beads on boiler – resp. pipe steel and heat – treatable steel of similar alloy .

Suitable for following base materials:
13CrMo22, 15CrMo3, MoV42

At 720 ºC
T: 590 – 690 N/mm²
Y: 480 – 510 N/mm²
E(1=5d): 18 – 22 %
—————-
At 930 ºC
T: 480 – 590 N/mm²
Y: 340 – 390 N/mm²

E: 20 – 24 %

–

Lime basic coated electrode for high quality weld beads on boiler – resp. pipe steel and heat – treatable steel of similar alloy.

–

Basic coated electrode for high-tensile fine grain constructional steel . The weld deposit has high tensile strength and is resistant to cracks. Ductile up to -60 ºC.

AWS: E 9013 G
ISO 3580: E 2 Cr Mo R
DIN 8575:E Cr Mo 2 R 22

BS: 2493 Type C

Current: = (+) / ~

C: 0,07 %
Si: 0,35 %
Mn: 0,65 %

Cr: 2,3 %

Mo: 1 %

Rutile basic coated electrode for high temperature – stressed parts in boiler and pipeline construction at working temperatures up to 600 ºC.

Suitable for base materials:
10 Cr Mo 9 10, 10 Cr SiMoV 7

At 760 ºC
T: 630 – 680 N/mm²
Y: 490 – 540 N/mm²
E(1=5d): min 20 %

I: 80 Joule
————–
At 950 ºC
T: 540 – 640 N/mm²
Y: 440 – 490 N/mm²

E(1=5d): 20 %

I: 80 Joule

–

Lime basic coated electrode for high temperature – stressed parts in boiler and pipeline construction at working temperatures up to 600 ºC.

AWS: E 502 – 15
ISO 3580: E 5 Cr Mo B
DIN 8575: E Cr Mo 5 B 20+

Current: = (+) / ~

C: 0,07 %
Si: 0,5 %
Mn: 1 %

Cr: 5,1 %

Mo: 0,5 %

Lime basic coated electrode for high temperature -steel in boiler construction. The weld deposit is heat-treatable.

Suitable for following base materials:
10 CrMo 19 5
and the steel downpour identical to kind.

At 760 ºC
T: 640 – 730 N/mm²
Y: 490 – 540 N/mm²
E(1=5d): 18 – 22 %

I: 110 Joule
————-
At 960 ºC
T: 590 – 690 N/mm²
Y: 470 – 540 N/mm²

E(1=5d): 18 – 22 %

I: 110 Joule